What causes Pattern Braided Sleeve to become brittle?

With the widespread use of Pattern Braided Sleeve, various Pattern Braided Sleeve may be used in every corner of life. Although these Pattern Braided Sleeve look inconspicuous, they can also play a very important role. However, some Pattern Braided Sleeve are easy to become brittle during use. After becoming brittle, the Pattern Braided Sleeve can no longer be used, so many people It feels like a headache.

In fact, the root cause of the brittleness of the Pattern Braided Sleeve is: the essential reason for the Cable Sleeve material. After the Cable Sleeve product reaches a hardness of 60 degrees or more, its tear resistance and elasticity will plummet, resulting in the Pattern Braided Sleeve. become very brittle. So if you want the Pattern Braided Sleeve to be less brittle, try to make the hardness below 60 degrees.
Another thing to talk about is the production problem. During the production and processing of the Pattern Braided Sleeve, it will be heated to a certain temperature, but if the temperature control is not high or the heating time is too long, the Pattern Braided Sleeve will become brittle. In addition, in the process of use and storage, not being able to maintain good ventilation, or the secondary vulcanization time is too long will also cause this phenomenon, and the most important thing is the material problem of the pattern woven sleeve itself. If not, the tear resistance cannot be achieved, so the Pattern Braided Sleeve becomes weak.
In addition to these, the brittleness of Pattern Braided Sleeve is also related to the design of the mold. If the mold design is unreasonable or the production structure is unreasonable, it may cause the Pattern Braided Sleeve to crack the mold during the production process. , if this phenomenon really occurs, the Pattern Braided Sleeve produced will naturally become brittle, so before production and processing, it is necessary to try to improve the processing or mold structure.
The above is one of the main reasons for the brittleness of the Pattern Braided Sleeve. In addition, during use, if the ambient temperature is too low or the use time is too long, aging has occurred, which will also cause the Pattern Braided Sleeve to become brittle. For braided sleeves, after a period of use, the product should be replaced in time when the product is aging.